treebeard wrote:

On Sun, 05 Jun 2005 20:47:44 -0400, treebeard
treebeardentmootatyahoodotcom wrote:


http://www.handyharmancanada.com/The...tm#Braze%20650


(tig-brazing stainless steel 316L , would the following filler work?)
(forgot to say what I would be brazing)


Filler Metal name: Braze 655
Typical Applications: For brazing Invar, Kovar and similar alloys to
copper in vacuum tubes; as jet engine rubbing seals.
Solidus: 1385'F/750'C
Liquidus: 1560'F/850'C
Max. Recom. Brazing Temp. 'F: 1700
Nominal Composition,%: 65Ag 28Cu 5Mn 2Ni
Joint Color as Brazed: White
Density Troy oz/cu in: 5.20
Electrical Characteristics

* Conduct. % IACS: 12.8
* Resistivity microhm-cm: 13.4



I know from reading Ernie's posts Silicon Bronze is recommended (not
the low fuming kind)


Why not use 316L SS wire as filler ?

Martin

--
Martin Eastburn
@ home at Lion's Lair with our computer lionslair at consolidated dot net
NRA LOH, NRA Life
NRA Second Amendment Task Force Charter Founder

----== Posted via Newsfeeds.Com - Unlimited-Uncensored-Secure Usenet News==----
http://www.newsfeeds.com The #1 Newsgroup Service in the World! 120,000+ Newsgroups
----= East and West-Coast Server Farms - Total Privacy via Encryption =----

On Sun, 05 Jun 2005 23:20:41 -0500, "lionslair at consolidated dot
net" "lionslair at consolidated dot net" wrote:

treebeard wrote:

On Sun, 05 Jun 2005 20:47:44 -0400, treebeard
treebeardentmootatyahoodotcom wrote:


http://www.handyharmancanada.com/The...tm#Braze%20650


(tig-brazing stainless steel 316L , would the following filler work?)
(forgot to say what I would be brazing)


Filler Metal name: Braze 655
Typical Applications: For brazing Invar, Kovar and similar alloys to
copper in vacuum tubes; as jet engine rubbing seals.
Solidus: 1385'F/750'C
Liquidus: 1560'F/850'C
Max. Recom. Brazing Temp. 'F: 1700
Nominal Composition,%: 65Ag 28Cu 5Mn 2Ni
Joint Color as Brazed: White
Density Troy oz/cu in: 5.20
Electrical Characteristics

* Conduct. % IACS: 12.8
* Resistivity microhm-cm: 13.4



I know from reading Ernie's posts Silicon Bronze is recommended (not
the low fuming kind)


Why not use 316L SS wire as filler ?

Martin

If you do a google group search on tig braze-welding, you'll find the
details. TIG-Braze Welding - Chapter 3 would be a good thing to
search for (sci.engr.joining.welding newsgroup), but there are a lot
of messages about tig braze-welding.

Using 316L ss wire as filler would be regular welding, and the base
metal would melt or be distorted.

Using the silicon bronze, which has a lower liquidus point, the base
316L ss would not be melted or heat distorted very much, depending on
the amount of heat applied. The result would be a "braze weld" or
whatever you want to call it - I don't want to get in semantics
argument.

316L physical properties:
Physical Data

Electrical Resistivity (microhm-cm (at 68 Deg F)) 444

Melting Point (Deg F) 2550

Modulus of Elasticity Tension 28

For what I plan to do, considering my non-skill level, brazing with
oxy-acet and the Meco torch and the appropriate filler is a probaly
the way for me to go, from what I've learned from the folks in this
newsgroup. But, tig has been mentioned as a good alternative
and....so I've been reading.