What kinda plastic do I have?!
The current American Woodworker has an article on making clear router
baseplates. And... I found a large sheet of 1/4" clear plastic at a garage sale yesterday. So I decided to make a base. The plastic cut, drilled, and routed very easily, with none of the brittleness I associate with acrylic; so I figured it must be polycarbonate (which I have not used before). The article says to use either acrylic or polycarbonate, and to "flame finish" it. As soon as I touched it with the flame, it caught on fire! (actually I tested it on a piece of scrap first, so nothing was lost...) So what kinda plastic do I have? If acrylic and polycarb can be flame finished, then I must have something different? |
#2
Posted to rec.woodworking
|
|||
|
|||
What kinda plastic do I have?!
Toller wrote: The current American Woodworker has an article on making clear router baseplates. And... I found a large sheet of 1/4" clear plastic at a garage sale yesterday. So I decided to make a base. The plastic cut, drilled, and routed very easily, with none of the brittleness I associate with acrylic; so I figured it must be polycarbonate (which I have not used before). The article says to use either acrylic or polycarbonate, and to "flame finish" it. As soon as I touched it with the flame, it caught on fire! (actually I tested it on a piece of scrap first, so nothing was lost...) So what kinda plastic do I have? If acrylic and polycarb can be flame finished, then I must have something different? Without knowing more, I can't tell if it's flammable or inflammable plastic. :-) Seriously, it's probably acrylic. Flame polishing is a tricky business. Touching the flame to the plastic will very likely ruin it.Here are some other ideas for smoothing edges: http://www.finishing.com/68/50.shtml |
#3
Posted to rec.woodworking
|
|||
|
|||
What kinda plastic do I have?!
One way of identifying the two is to look at the edge. If it
is clear, it's acrylic. If it has a blue tint, it's polycarbonate. Frank "Toller" wrote in message ... The current American Woodworker has an article on making clear router baseplates. And... I found a large sheet of 1/4" clear plastic at a garage sale yesterday. So I decided to make a base. The plastic cut, drilled, and routed very easily, with none of the brittleness I associate with acrylic; so I figured it must be polycarbonate (which I have not used before). The article says to use either acrylic or polycarbonate, and to "flame finish" it. As soon as I touched it with the flame, it caught on fire! (actually I tested it on a piece of scrap first, so nothing was lost...) So what kinda plastic do I have? If acrylic and polycarb can be flame finished, then I must have something different? |
#4
Posted to rec.woodworking
|
|||
|
|||
What kinda plastic do I have?!
You probably do have polycarbonate. Try taking a strip of the scrap and
bending it. If it snaps, its acrylic. If it bends, its poly. The stuff burns well, as you found out. Flame polishing is tricky. Don't actually touch the flame to the plastic. Just get close. "Toller" wrote in message ... The current American Woodworker has an article on making clear router baseplates. And... I found a large sheet of 1/4" clear plastic at a garage sale yesterday. So I decided to make a base. The plastic cut, drilled, and routed very easily, with none of the brittleness I associate with acrylic; so I figured it must be polycarbonate (which I have not used before). The article says to use either acrylic or polycarbonate, and to "flame finish" it. As soon as I touched it with the flame, it caught on fire! (actually I tested it on a piece of scrap first, so nothing was lost...) So what kinda plastic do I have? If acrylic and polycarb can be flame finished, then I must have something different? |
#5
Posted to rec.woodworking
|
|||
|
|||
What kinda plastic do I have?!
On 4-Feb-2006, "Toller" wrote: The article says to use either acrylic or polycarbonate, and to "flame finish" it. Don't bother - just sand it with ever finer grits until you get a finish you like. If you want it really clear, use a polishing compound. You can use the stuff that is sold for finishing gelcoat on boats or repairs on cars. For really fine finish, you can use the finest polishing compounds for glass or metal. A Dremel with a small buffing wheel can speed things up. Mike |
#6
Posted to rec.woodworking
|
|||
|
|||
What kinda plastic do I have?!
In article ,
"Toller" wrote: So what kinda plastic do I have? If acrylic and polycarb can be flame finished, then I must have something different? Did the 'fire' continue to burn, after you removed the flame? Or did it go out after you removed the flame? In the countertop business, acrylic material won't burn by themselves. Polyester (which can also be completely clear) will continue to burn after the starting flame has been removed. The edge colour, as pointed out by another reader, can give you some guidelines. Acrylic, polyester, and polycarbonate all smell different too. Polyester smells like fibreglass. Brittleness, is not an indication of acrylic as it is les brittle than polyester...but I do not know about polycarbonate. Odds are that 1/4" clear plastic at a garage sale won't be polycarbonate as it is ghastly expensive. My bet is that you have a piece of of basic plexiglass. Plexiglas is the same chemically as Lucite: poly(methyl methACRYLate). Polycarbonate is Lexan. Another hint is that plexiglass is almost always 1/4". HTH |
#7
Posted to rec.woodworking
|
|||
|
|||
What kinda plastic do I have?!
"Robatoy" wrote in message ... In article , "Toller" wrote: So what kinda plastic do I have? If acrylic and polycarb can be flame finished, then I must have something different? Did the 'fire' continue to burn, after you removed the flame? Or did it go out after you removed the flame? In the countertop business, acrylic material won't burn by themselves. Polyester (which can also be completely clear) will continue to burn after the starting flame has been removed. The edge colour, as pointed out by another reader, can give you some guidelines. Acrylic, polyester, and polycarbonate all smell different too. Polyester smells like fibreglass. Brittleness, is not an indication of acrylic as it is les brittle than polyester...but I do not know about polycarbonate. Odds are that 1/4" clear plastic at a garage sale won't be polycarbonate as it is ghastly expensive. My bet is that you have a piece of of basic plexiglass. Plexiglas is the same chemically as Lucite: poly(methyl methACRYLate). Polycarbonate is Lexan. Another hint is that plexiglass is almost always 1/4". Not blue, but it lit very easily and continued to burn vigorously after I removed the torch. Polyester? Didn't know that was a possibility. |
#8
Posted to rec.woodworking
|
|||
|
|||
What kinda plastic do I have?!
On 5-Feb-2006, "Toller" wrote: Not blue, but it lit very easily and continued to burn vigorously after I removed the torch. Polyester? Didn't know that was a possibility. Polyester is common - Mylar is a brand name and is in sheet form. Vivak is another brand. Clear plastic pop bottles are a type of polyester. There are lots of other plastics. Polystyrene burns easily - are you sure it's not polystyrene? Mike |
Reply |
Thread Tools | Search this Thread |
Display Modes | |
|
|
Similar Threads | ||||
Thread | Forum | |||
Soil Pipe - Plastic on to castiron | UK diy | |||
Are push fit plumbing fittings any good? | UK diy | |||
SKYLIGHTS: Choice of flat glass or plastic dome | Home Repair | |||
Help! Sun damage & plastic tarp melted onto dining room table | Woodworking | |||
Plastic Pipes in central heating | UK diy |