Phil Addison wrote:
You have correctly pointed out that using a *damp* cloth
prematurely while [a soldered pipe joint is]hot will cause
crystallization. On the other hand I pointed out that using
a *dry* cloth on *Fluxite* type flux when still quite hot
makes it easier to clean off. I don't see any conflict here.
The point about not disturbing the joint until it has set is
valid in all situations.

QED.