Phil Addison wrote:
Solder for capillary fittings is tin-rich and does not have a
pasty phase.

No? Not at all? In that case, if you heat up a test join and
continually move it as the solder solidifies, the joint strength
won't be compromised - is that what you're saying?


__________________________________________________ ______________
Sent via the PAXemail system at paxemail.com