Just had my Roadster front fenders dipped. Worked well; leaves the Bondo
as a dark gray, porous, leached out material that can be easily removed.
Same for lead. After the dip, the metal will rust very quickly if not
protected. I believe it is muriatic acid that is used.
JR
Dweller in the cellar

Unknown wrote:
Apparently there is a dip process for taking automotive painted parts
to the bare metal.

Question? Anyone know the chemicals in the dip?



--
--------------------------------------------------------------