Don't get the wrong impression, Wayne. I'm not hot, nor was I upset by your
response. Just adding more comments to what is a good conversation and a
learning experience for everyone that isn't familiar. I figure you and I
have exchanged views long enough that we understand one another.

Agreed.

To quote what you said earlier:

I'm afraid I'll have to disagree at least a little in this
statement. I actually believe that 4140 was developed to be a high
strength material that could be welded reliably.

The material in question here is actually 4130, not 4140 or the others
(4340 is chrome nickel moly). 4130 is low enough in carbon that it won't
heat treat hard enough to create the problems the others do, and *can* be
welded reliably.

Ok. I'll buy that. All of my higher alloy stock like that is unknown
so I can't pin down the exact alloy. Experience has taught me how to
recognize that it's one of the chrome molly alloys when I do run
across it though.