I've sprayed WB Varathane with sat results. Have you tried it?

On Wed, 20 Jul 2005 15:01:44 -0700, David wrote:

Bubba wrote:
The "(ugh) poly" tells me something. I'm open to ideas. What is the
objection to poly? What are viable alternatives. The surface will be used
as a tray and from time to time will be exposed to a variety of liquids
including alcohol.


"David" wrote in message
...

Bubba wrote:


I've been trying my hand at veneer inlays. Deft spray laquer seems to
give a great looking finish, but I doubt if it would stand under wet
drinks. Any ideas as to how polyurethane as a protective top coat would
bond to a laquer finish

Not very well over the long term. How's 'bout scuffing the lacquer, apply
dewaxed shellac, and then the (ugh) poly?

dave



The "ugh" was for the application; not for the results. Some guys will
tell you poly looks bad. I don't think that's true unless you pile it
on. But for application, I prefer spraying water bornes. They can be
recoated in under 40 minutes and don't stick to everything around the
spray area. Brushing poly often results in bubbles and it dries too
slowly for me. Thin the poly to reduce bubbles. Spraying it makes on
heck of a mess due to the sticky residue of overspray. Dust can settle
on a slow drying finish like poly. I can't recall seeing any
appreciable dust nibs on my water borne finishes. But the poly is gonna
be more water resistant than WB even with Crosslinker added so I can
appreciate why you'd choose poly. I've got a poly'd desktop that is
softer (after more than a year after the finish was applied) than
WB/Crosslinker that has set for a couple of weeks, BUT the poly does
better on the water torture test...

Dave