thin strong partition wall - followup
sm_jamieson wrote:
wrote:
sm_jamieson wrote:
Previously it was decided that the best approx 1" thick partition would
be a 1" thick fibre cement panel, which would be very stiff and strong.
Well, what I have decided to do is render-up a panel (vertically) to
approx this thickness against a ply former and mesh etc. But I want the
mix to be almost fibre-cement concrete, so it's very strong. What mix
of cement, sharp sand, fibres and aggregate would be best to us ? The
result should be very strong but also render-able without all aggregate
sinking to the bottom etc.
Cheers,
Simon.
3:1 sand:cement, as this gives the strongest end result. Stronger mixes
will microcrack during cure, thus weakening.
5% chopped alkali-resistance glass fibre will give you proper fibre
reinforced cement. There are other fibre options too, but this is whats
mostly used now that the asbestoses are out of fashion.
Any idea where to get the glass fibre from ? Not having much luck on
the web.
Cheers,
Simon.
Also, what about polypropylene fibres - these seem to be used in
ready-mix fibre reinforced concrete ?
Simon.
|