Default Thinning ratio for precat lacquer?

Finally picked up some Pre-cat lacquer to expand my
horizons. First attempt demonstrates it needs to be
thinned. From the sources I've found in books, I'm under
the impression that it's treated like regular nitro as far
as thinning goes. Is that correct? Today I sprayed it at
80 degrees, high humidity (unusual for northern Cal) with
HVLP. I couldn't get flow out without putting on so much
the result is that dreaded "plastic" look.

I've e-mailed the mfg. for viscosity cup timings but in the
meantime (and WITHOUT A cup) I'm looking for GENERAL
guidelines as to thinning ratios. 10-20%?

What's about the max you can thin this stuff? Ratio for
first 2 coats and ratio for topcoat? I'm thinking I should
go with thinning before I consider a retarder; correct?

David

  #2   Report Post  
David
 
Posts: n/a
Default Thinning ratio for precat lacquer?

Observation: the finish is quite soft after 8 hours. I
sprayed a sample board with Enduro WB poly and it's MUCH
harder than the lacquer.

Question: Granted, the lacquer was applied heavier than
ideal, but shouldn't a lacquer be hard enough not to peel
off with my fingernail after 8 hours??

There is no mfg. date on the can that I can find; something
I read tonight indicated (Flexner's book, IIRC) mentions
checking the date on pre-cat lacquer cans. Kinda like
canned shellac (drying problems, if it's too old)?

David

David wrote:

Finally picked up some Pre-cat lacquer to expand my horizons. First
attempt demonstrates it needs to be thinned. From the sources I've
found in books, I'm under the impression that it's treated like regular
nitro as far as thinning goes. Is that correct? Today I sprayed it at
80 degrees, high humidity (unusual for northern Cal) with HVLP. I
couldn't get flow out without putting on so much the result is that
dreaded "plastic" look.

I've e-mailed the mfg. for viscosity cup timings but in the meantime
(and WITHOUT A cup) I'm looking for GENERAL guidelines as to thinning
ratios. 10-20%?

What's about the max you can thin this stuff? Ratio for first 2 coats
and ratio for topcoat? I'm thinking I should go with thinning before I
consider a retarder; correct?

David


  #3   Report Post  
Todd Fatheree
 
Posts: n/a
Default Thinning ratio for precat lacquer?

David" wrote in message
...
Finally picked up some Pre-cat lacquer to expand my
horizons. First attempt demonstrates it needs to be
thinned. From the sources I've found in books, I'm under
the impression that it's treated like regular nitro as far
as thinning goes. Is that correct? Today I sprayed it at
80 degrees, high humidity (unusual for northern Cal) with
HVLP. I couldn't get flow out without putting on so much
the result is that dreaded "plastic" look.

I've e-mailed the mfg. for viscosity cup timings but in the
meantime (and WITHOUT A cup) I'm looking for GENERAL
guidelines as to thinning ratios. 10-20%?

What's about the max you can thin this stuff? Ratio for
first 2 coats and ratio for topcoat? I'm thinking I should
go with thinning before I consider a retarder; correct?

David


Pre-cat laquer definitely has a shelf life, and it's a lot less than
shellac. When I bought the Sherwin Williams flavor of precat, they put a 6
month use-by date on the can. I have no idea what the results would be of
using a batch of precat after the catalyst has "worn off" so to speak.

todd


  #4   Report Post  
David
 
Posts: n/a
Default Thinning ratio for precat lacquer?

Thanks, Todd. I'll call the store tomorrow to see what
their story is on this stuff.

David

Todd Fatheree wrote:

David" wrote in message
...

Finally picked up some Pre-cat lacquer to expand my
horizons. First attempt demonstrates it needs to be
thinned. From the sources I've found in books, I'm under
the impression that it's treated like regular nitro as far
as thinning goes. Is that correct? Today I sprayed it at
80 degrees, high humidity (unusual for northern Cal) with
HVLP. I couldn't get flow out without putting on so much
the result is that dreaded "plastic" look.

I've e-mailed the mfg. for viscosity cup timings but in the
meantime (and WITHOUT A cup) I'm looking for GENERAL
guidelines as to thinning ratios. 10-20%?

What's about the max you can thin this stuff? Ratio for
first 2 coats and ratio for topcoat? I'm thinking I should
go with thinning before I consider a retarder; correct?

David



Pre-cat laquer definitely has a shelf life, and it's a lot less than
shellac. When I bought the Sherwin Williams flavor of precat, they put a 6
month use-by date on the can. I have no idea what the results would be of
using a batch of precat after the catalyst has "worn off" so to speak.

todd



  #5   Report Post  
Preston Andreas
 
Posts: n/a
Default Thinning ratio for precat lacquer?

I've been shooting Magnamax from ML Campbell. The catalyst is added when
you buy it and it is good for 90 days. They have strict recommendations for
thinning and adding retarder, including using only their products for the
thinner and retarder. There is also Magnalac where the catalyst is added at
the factory. The shelf life is much longer.

In other words, each product from each manufacturer is different. It is
best to call their 800 number and talk to tech if you have any questions. I
find that all dealers may talk like they really know their product, but
sometimes they may not be as knowledgeable as they lead you to believe.
That is why I get what information I can from their literature and off their
website, then call tech if I have any remaining questions.

Preston
"David" wrote in message
...
Finally picked up some Pre-cat lacquer to expand my
horizons. First attempt demonstrates it needs to be
thinned. From the sources I've found in books, I'm under
the impression that it's treated like regular nitro as far
as thinning goes. Is that correct? Today I sprayed it at
80 degrees, high humidity (unusual for northern Cal) with
HVLP. I couldn't get flow out without putting on so much
the result is that dreaded "plastic" look.

I've e-mailed the mfg. for viscosity cup timings but in the
meantime (and WITHOUT A cup) I'm looking for GENERAL
guidelines as to thinning ratios. 10-20%?

What's about the max you can thin this stuff? Ratio for
first 2 coats and ratio for topcoat? I'm thinking I should
go with thinning before I consider a retarder; correct?

David





  #6   Report Post  
David
 
Posts: n/a
Default Thinning ratio for precat lacquer?

I DID get a callback from the mfg and was told to use 10-15%
acetone (I'm in CA) PLUS retarder to counteract the faster
drying of adding acetone. I got good results today from
just thinning the lacquer about 15% at 76 degrees.

David

Preston Andreas wrote:

I've been shooting Magnamax from ML Campbell. The catalyst is added when
you buy it and it is good for 90 days. They have strict recommendations for
thinning and adding retarder, including using only their products for the
thinner and retarder. There is also Magnalac where the catalyst is added at
the factory. The shelf life is much longer.

In other words, each product from each manufacturer is different. It is
best to call their 800 number and talk to tech if you have any questions. I
find that all dealers may talk like they really know their product, but
sometimes they may not be as knowledgeable as they lead you to believe.
That is why I get what information I can from their literature and off their
website, then call tech if I have any remaining questions.

Preston
"David" wrote in message
...

Finally picked up some Pre-cat lacquer to expand my
horizons. First attempt demonstrates it needs to be
thinned. From the sources I've found in books, I'm under
the impression that it's treated like regular nitro as far
as thinning goes. Is that correct? Today I sprayed it at
80 degrees, high humidity (unusual for northern Cal) with
HVLP. I couldn't get flow out without putting on so much
the result is that dreaded "plastic" look.

I've e-mailed the mfg. for viscosity cup timings but in the
meantime (and WITHOUT A cup) I'm looking for GENERAL
guidelines as to thinning ratios. 10-20%?

What's about the max you can thin this stuff? Ratio for
first 2 coats and ratio for topcoat? I'm thinking I should
go with thinning before I consider a retarder; correct?

David





Reply
Thread Tools Search this Thread
Search this Thread:

Advanced Search
Display Modes

Posting Rules

Smilies are On
[IMG] code is On
HTML code is Off
Trackbacks are On
Pingbacks are On
Refbacks are On


Similar Threads
Thread Thread Starter Forum Replies Last Post
spray paint vs hand paint wendi Home Repair 19 July 21st 04 02:36 PM
new minwax lacquer? Mike S. Woodworking 1 April 2nd 04 10:03 PM
Poly over Lacquer? Bay Area Dave Woodworking 5 November 5th 03 04:14 PM
Source for Black Laquer Ron Woodworking 14 October 24th 03 11:41 AM


All times are GMT +1. The time now is 07:01 AM.

Powered by vBulletin® Copyright ©2000 - 2024, Jelsoft Enterprises Ltd.
Copyright ©2004-2024 DIYbanter.
The comments are property of their posters.
 

About Us

"It's about DIY & home improvement"