Hi.
Just had a small sheet of .5mm thick stainless steel 305 delivered for a project I'm starting. I expected it to be compatible with neodymium magnets. But nope! Am I missing something? Thanks. |
Neodymium magnet puzzlement
On 15/10/2020 18:36:18, Arthur 51 wrote:
Hi. Just had a small sheet of .5mm thick stainless steel 305 delivered for a project I'm starting. I expected it to be compatible with neodymium magnets. But nope! Am I missing something? Yes, stainless steel 305 is non-magnetic. https://www.aksteel.com/sites/defaul...less-steel.pdf |
Neodymium magnet puzzlement
FFFF****!
Thanks. |
Neodymium magnet puzzlement
On Thursday, 15 October 2020 18:45:39 UTC+1, Arthur 51 wrote:
FFFF****! Thanks. Paint it reddish-purple. Won't actually help but could make it magentic. |
Neodymium magnet puzzlement
On 15/10/2020 18:45:36, Arthur 51 wrote:
FFFF****! Thanks. Some stainless steels are magnetic, perhaps armed with that knowledge you can get what you need? |
Neodymium magnet puzzlement
On 15/10/2020 19:47, polygonum_on_google wrote:
On Thursday, 15 October 2020 18:45:39 UTC+1, Arthur 51 wrote: FFFF****! Thanks. Paint it reddish-purple. Won't actually help but could make it magentic. :) |
Neodymium magnet puzzlement
In what way? If you mean non ferrous, that very much depends on the sort of
Stainless it is. We used to have many debates about this issue at Racal Marine. You or probably going to get involved in spec numbers and standards if you want it to be really non ferrous. You don't have this with Ally sheet! The reason Racal were upset was the radar system can be near the compass, requiring a re calibrate if it has any residual magnetism. Brian -- This newsgroup posting comes to you directly from... The Sofa of Brian Gaff... Blind user, so no pictures please Note this Signature is meaningless.! "Arthur 51" wrote in message ... Hi. Just had a small sheet of .5mm thick stainless steel 305 delivered for a project I'm starting. I expected it to be compatible with neodymium magnets. But nope! Am I missing something? Thanks. |
Neodymium magnet puzzlement
In message , "Brian Gaff (Sofa)"
writes In what way? If you mean non ferrous, that very much depends on the sort of Stainless it is. We used to have many debates about this issue at Racal Marine. You or probably going to get involved in spec numbers and standards if you want it to be really non ferrous. You don't have this with Ally sheet! The reason Racal were upset was the radar system can be near the compass, requiring a re calibrate if it has any residual magnetism. In my limited experience, SS which can be hardened is magnetic. The blades of our cutlery knives are magnetic but not the handles. -- Tim Lamb |
Neodymium magnet puzzlement
On Thursday, 15 October 2020 21:32:34 UTC+1, Fredxx wrote:
On 15/10/2020 18:45:36, Arthur 51 wrote: FFFF****! Thanks. Some stainless steels are magnetic, perhaps armed with that knowledge you can get what you need? Perhaps Wiki would help? https://en.wikipedia.org/wiki/Stainl...tic_properties |